DESCRIPTION
SEPS is formed by selective hydrogenation of styrene and isoprene copolymer. Compared with SEBS, SEPS elastomer has fast oil absorption speed, low surface viscosity after oil absorption, high hardness and tensile strength, small permanent deformation at break, and good adhesion to various polar and non-polar materials.
SEBS YH-4051 could be used in medical products, soft rubber toys, window grilles, TPE granulation, halogen-free flame retardant cable coating materials .
SPECIFICATIONS
| Appearance | White Powder |
| Volatility (%) | <=1.0 |
| Stress at 300% (MPa) | >=4.0 |
| Tension Strength (MPa) | >=20.0 |
| Elongation at Break (%) | >=500 |
| Hardness (Shore A) | 75~85 |
| Solution Viscosity @ (15%, 25℃) (mPa·s) | 400 |
| MFR @ (5kg, 200℃) (g/10min) | 0.10~0.50 |
| Permanent Deformation (%) | <=32 |
| Yellow Index | <=5.0 |
APPLICATION
High-resiliency glues, Jelly candles